冷挤压钢的球化退火工艺规范

HEATS

; q5 u( l" m8 D6 k3 F1 Q3 N2 ?5 o+ r5 a7 R; h: J; s! a- d y& _5 [% Z' Y6 q1 D( ^* Y- O6 r1 n: ~" e; j" y4 U* f& J ]8 L0 i# T* ~* Z; U& l, z4 }( @! w! |0 B3 I$ p- G9 U- p, T# a I0 p; ~5 u8 g; r: Q. V( b0 K& j# x1 W! H- p! T3 \& v$ i, H$ x3 p7 z: t, i8 t" Z" {7 H& J8 P9 Y k- b- m; b1 l9 k( m" |& w$ Z+ {1 ?3 {* c A/ ]' C6 M3 T- [5 F8 M) P; c! e. {, C9 c, P! Q t' }+ h; I4 E# p) D4 m3 B/ v t# f U7 b( F- W. r$ Z0 |$ d) h/ R) _4 j: ~+ y* q: _, O0 z& z+ `, k; d! f( k+ z4 C6 z- t% [& S, |! v: Z& n$ o3 h9 L. v3 v" x) H: o* ]$ S; n( G4 H2 r9 V0 T+ U! d' {' [& ?# I9 R( T0 \ A# _+ L8 A6 v: x I& a9 h: Z/ { l2 x& v. U1 V# v& P. E) e) M/ w5 c1 f6 [; d1 @4 J# H" C% J+ t% g( u& j e" `, a6 H* }/ ^+ y. [' V8 z. R% Q3 ]' u# c% J: t5 z2 j6 s7 w. u5 r& k7 T% P4 Q7 }, r" k1 L2 w9 C b3 s- E+ m a, _# ]% h7 k3 A8 U( f( s' n, _+ A4 I" e8 o9 t. \& E% ^5 `+ h0 X# p. i# P% l8 f9 u9 f' W; b1 b6 u+ l+ f8 P$ N: @: x8 M) j, @/ ~2 H! M+ w3 Z) L; Y7 Q: C3 P2 M" W$ `! \/ f/ j# X+ D+ h0 c4 ?

钢 号	退火前硬度（HB）	加热温 度（℃）	保温时间（h）	等温温度及时间（℃-h）	冷却速度（℃/h）	出炉温度（℃）	退火后硬度（HB）
15Cr,20Cr	170	860±10	3～4	-	<50	<130	300
15Cr,20Cr	170	780±10	2～3	700±10-6～8		125～131	500
15Cr,20Cr	170	720	5～6	-	<50	≤125	450
35,45,40MnB	>180	720	6～7	-	<50	≤145	550
08,15,20	150～180	720	2～3	-	空冷	≤120	-
20MnV,40Cr,50	187～217	950～1000	1～1.5	700-2～2.5	60	140	500
40Cr	-	770±10	4～5	670±10-5～6	炉冷	≤160	500