低碳钢、奥氏体不锈钢缝焊的焊接工艺参数

HEATS

: X/ Z+ x: |# R3 N$ a% r$ j$ h* U/ H F& N3 |, l, S3 I9 b' x3 W% u- R7 `5 K) \9 {' O; |; b& o! d9 x$ r6 v: S# Q, [7 g6 `# B* X* G6 ~8 A% F3 |* {+ G. k7 `9 l0 o9 `# U$ c4 C* v, Q! _/ r+ z$ y' G& a4 m" g& G$ f' I! d8 O8 H- _, Y" A3 q. z) L: g8 K$ e6 x1 u' m# k. N1 S( c$ ~: A% \% `0 O/ [' R6 [3 I! U8 w3 |2 I7 ^) B5 u- z5 O8 q: R; d: N) q( u2 b. o, Y8 t9 f# `9 u8 z5 C3 I9 h! S5 N# G0 s" O& g( K4 X# M- X* ?; R2 g3 Y2 d( o6 a0 o! K0 d0 S6 O' U3 x0 g) N/ Q* k8 Z0 } M j6 J6 L* Q$ p$ ~9 I1 n3 X8 Q5 @6 O" [$ A' `# j! z1 B& ~5 j+ k7 P& |+ b" U& ~ T2 f! l: w: S' S$ ~. w7 j( o {8 B6 C& h6 p) G+ {& F7 P' y# T H- N* u$ y) F) |" s) a! K9 Z3 \$ V7 S1 m5 n A, f2 J6 _: J. |. d d% J) G& F" r4 ]2 \0 u0 E0 s% D+ G7 r& x& @, C6 |* ^% v( B5 q z2 n: G8 M: Z$ B3 M$ C* j5 l' t# F1 k u/ I \0 x/ X6 `' ?1 p7 f% h& v7 G( }8 Z' d( N0 X/ S6 O+ _9 J+ i- q0 ?% }* O' @$ w5 H8 L, o3 p0 a# K8 v7 m9 p- }/ Z) F& `! Y- B0 d+ }. y2 f5 S# { K" O0 H1 V' `# [* N* O$ o9 D% `" X! |* g( b* i! L$ c, A2 ^9 j) y0 l( k* b8 {& G9 H2 ~+ h6 p) X5 R% l4 A8 u! I0 b- H* W, p; N$ m- ^) k2 I( ]; d. B4 s J+ u8 X, g; I: ` x5 D! Z+ o8 F8 `' \) ~1 U9 r' F( B l- u, E7 g' n4 u \0 a: @- t# s9 ~8 @4 T2 y( Z4 f/ b7 q% T5 g6 e* E: b5 @! z0 u) S: {2 y& R/ U6 b# ]4 L) o# e9 Q: Q( c9 G3 w0 k) h& m" Q( y5 w/ h. s- j2 w5 Z( Y; X" B& U) F1 P9 l+ m6 g* h+ a0 p8 R3 H: V! j' m: e9 f( C4 l. \# x+ ?9 q: z, ]# S5 h( t1 n0 f8 d+ L% e- `1 S7 X8 d/ d3 U# f6 v. h) I9 D6 _; n. Z6 s1 Z' S+ A% y, |: e G/ h" {' T; m8 w+ ^# \- ]: _/ J4 }5 I8 q' r6 z7 I1 ?& x' G* S* N7 _% i: t8 A3 w2 d8 u F( q& ^( W7 E8 E; l0 U( ]$ z. |: F; a* m ]9 k, t8 I5 |' f( r; i8 c; ]5 g& b+ S( b0 N y( y H& U ^. o& h# X6 T9 @5 k! @# P6 ? `- @1 Z9 L3 L* u# R" G) k* c: z) M, \4 c1 v/ W- P6 w4 i( `, {8 [' R# Q/ k2 S" N! N& G7 J1 z% t2 S7 Y! O: e' i& O# n3 e: b. s, L3 j& D3 R+ e n6 C' q$ K. ]) `1 |5 e, Q R- z; b$ h! g% ~3 W; H- u2 s$ D% |" O* P2 Y' C& `8 B* G O3 T+ P6 o! l0 p$ z" P) \0 f" j/ z/ B+ p) @0 I, ^9 m' z v) C! K7 o9 e1 e4 x( H" \; e2 W4 ~: S* B( }* O; n. K' R' H$ E% C4 y: q3 A! ?# ]+ @# t A5 Y }# G2 x) `- \7 Z+ n7 ~% t4 I/ [% t$ T: y4 V( z3 M/ b3 E+ z6 y' @* i+ h1 h3 T& {; H$ E* e/ q( ]3 M: a8 a: Z% s1 r9 E- B) L6 B, S2 t/ E- P2 j. _$ a) n4 Z% t9 R1 b$ L3 x& [, @( `- o o" l" O; y; u1 b. w a' f! N2 a! U3 G! S. ?9 F/ G7 }$ c* k8 }& c2 p" }8 {4 {; f* Y# {; J) {/ n0 w, x" d4 x7 l6 I$ B% ?9 V, e- V* [/ M9 E& {: c# ], J( v. u! L2 ^" y* Y; ]1 r: O" I2 Q9 t! u. ]& G$ @! I( v- Y5 X0 J8 c# y# p7 k$ k; x1 d" a1 c1 ^, m ]; ^% N* L' W5 ~9 ]6 v9 I3 C, N+ X! G5 \# t: F4 y1 x( [* j! z) Q( ]) C% \5 \* b8 l w+ R9 ]9 ]0 E8 K) k2 {" e$ J( n+ n4 A9 j& Q& j, N3 B: q2 W& S, R3 r% p; x8 B. g: H/ o& ]' d( H* i8 K h7 v( O; S. `8 L$ [( _$ C4 f$ f. [) } F1 {' X* t @+ \( E5 F' b) W8 B& N3 o' F, D" l" O- d7 k( z. K! q1 j+ ^" ]9 m7 B* k8 E0 E1 v9 X" G* g# i; c; _/ f, N' |! X+ o0 Q& \1 k9 N: u2 W( o( z- O+ e* `4 e* H6 q1 n+ m7 d: v h( n# ]+ _+ @" e! _; B7 G2 y4 n7 [5 Z" x, u3 e/ L. u$ q8 B( F" g7 L3 C2 U6 h8 y% i. _' C. S3 ]- w7 b9 M E4 V6 Q3 V" _5 i& V/ t/ c6 x6 ?) m0 g& s' d; F Z' L; I! Q* p+ F5 h" d$ |( o7 W4 A4 C! {( j+ x* s4 o; q8 D: p4 c5 k: j0 Z# F+ g8 c I- i3 b$ T6 S' p& W) l4 ?$ [) T' c$ X% t" C( I! h/ R, [, i F. q: v7 ]) h5 l F; \6 {6 z7 I9 k# e0 ?) c" S) P$ W. r% v8 B; y# q) |) [# E0 R" F2 P. F5 C+ G8 i$ `* S& O7 ^: c5 Z' y( l5 c& ?% j! g' Z! x# J! w" `6 d% f9 w' U- I6 i6 D7 V# C$ A. y+ D) ?% [5 X/ E: t9 s: i2 m: F A: `- T. F+ A% Q% L6 R B, M, E2 Y- J2 _) ~; F% }# v, ?3 J' P' @$ S, H9 E- J d: Z0 r- m1 f8 u0 B% z! h8 G. h9 }8 d/ B' U& G0 f/ g. b. k) o4 g) O; F% }5 a6 E0 R/ d# _9 N& |8 {9 ^& ^0 ?2 k" c# k8 n P# ~ r4 r9 p) H h$ {6 }) V Z' I( D; ~ P! q5 O' y4 P) Y( @; k6 H; `) C* v) q: [" T" s* D! S/ l) n; a% c) [ E4 K8 g8 p( a. f, B( U1 M0 T. u2 u- B4 K! m! E1 S/ l% x8 H) H0 W2 Z0 r. {8 O7 }/ \/ u9 q |( C% P, Z4 n6 M' x: L0 h/ j( Q. S G d; q8 V3 ~; Y Q: j: I @3 h8 N$ [. p. d* ]) G! T8 y/ `+ N! e J# m _: L: h$ V% J0 Z+ V: E8 F' F: R m! y+ z% g3 U$ Q+ n1 D5 N5 j( O8 T/ r2 M' u6 B( w+ k; @3 a5 t& l7 i* b! v2 K3 X. p& l" }6 ]. B/ j" S8 B( _% k1 V* O$ f m5 r) _8 N G7 |& p: H: Y2 v2 q* c/ Y1 ?4 T; E% x- h3 O6 d2 N4 N/ P& Y2 k+ T1 w: l- W" L4 g4 g' o1 _' h8 a( y: q% K2 J% m$ E& x$ V) N) Q1 g9 \5 x4 B9 ~+ y( M9 `0 O( Z: R3 l" g, [1 Z0 m* A6 z4 ]+ j; x( {# A; J+ `8 [+ e7 |3 J4 S2 t5 l. H! \/ A7 W/ @+ L* C% i; B/ ~+ [& l6 e* [: k4 J+ d! c$ b( ~8 { u' M# [9 l3 d: a* t2 c0 l" ]9 _' O9 P5 X! z2 u/ ?1 g. `: s: ~- E3 N5 w5 Z3 l, {' L5 h( R+ p& Y3 O0 m; _' ^; _8 Z; g* [ V5 F% n; N& t4 n6 o" X+ e& b, j: {/ S' e2 j: ^- P, J+ b7 H* x' L+ K* K2 j7 H D' j3 ?7 C6 h, e1 M' n8 I- l" v6 F" C' R. L& P/ s4 u% i1 ^' y& E5 n* y# u) n# ^ [; p" j5 ^, ?2 n% `: s3 D6 p3 [' Q' p( A) i! l, Y9 N$ E4 n& W# u4 F: i# C" T3 h% C; u, `: b# j0 e1 P& g$ R: x& N$ F8 p: a! p! @' _& r x4 t" e# f9 H; F" J, Q, q% _; T$ Y, |( K( t+ y* C; N* W& d% f/ n! W7 `' |+ P0 [4 c2 v; l" s k0 I! c4 r* i' u8 ~- c& w" \3 a k0 x B$ @0 G# y% e" g7 I) [, Q1 T# F% a3 {2 B# {% W N5 _8 I; D" _' ^6 y( C1 [4 A0 d/ N C( F, S2 ~4 U1 I$ { Q, ^; l$ H- n5 l0 I" v* v8 i( A1 N' n& ?3 G8 t2 ^/ Z1 L+ |: j2 w6 @8 P3 z- v( r. O( ^1 |% I0 A/ S; G. W& x6 K% H6 f3 y/ w3 u; P4 t" d" q/ U/ J+ W, W) y( W# B% ~1 A" V( ]8 R/ O. J+ j3 p) }# S. n* I% O) c3 d% `" E: g& p1 L3 M& I" i1 p6 J- ]6 A, }" G! G# i- H; T4 g9 V9 f) |7 x+ E8 @7 R9 A" k: Z$ s0 w& ~$ }) I/ Q, g( r% S' U6 Q2 I+ h$ C& ]( z7 ?+ O+ E* W. r* V* B: l l" f, `5 T- b0 e9 p. r ?0 q/ |) e/ M9 Q* j. ^/ G* u3 {" Y/ L& ]( j0 `+ b4 a& v) K! z5 U7 h: C" c7 W% e, y/ y5 P- S* P% ]- E/ i( C/ x& V& k4 Y' z! c4 q p+ G+ i4 w+ k0 N* U; |* H9 C3 I8 A/ e8 O: D6 M/ ~5 U! f1 D9 ?- F6 u9 O& _' D: B0 B( Y# L' K' Y- A/ s4 s/ W& e4 h7 ~0 ?) p& @( G5 `

材  料	等厚搭接板的板厚 (mm)	滚轮电极厚度D及表面宽度d① (mm)			电极压力 (N)	最小重叠宽度L (mm)	最小重叠宽度L② (mm)		气    密    焊    缝
									高  速  焊  接				中  速  焊  接				低  速  焊  接
		最小d	标准d	最小D			d用最小值时	d用标准值时	焊接通电时间③ (周波数)	休止时间 (周波数)	焊接速度 (m/min)	焊接电流 (A)	焊接通电时间 (周波数)	休止时间 (周波数)	焊接速度 (m/min)	焊接电流 (A)	焊接通电时间 (周波数)	休止时间 (周波数)	焊接速度 (m/min)	焊接电流 (A)
低碳钢	0.4	3.7	5.3	11	2200		7	10	2	1	2.8	12000	2	2	2.0	9500	3	3	1.2	8500
低碳钢	0.6	4.2	5.9	12	2800		8	11	2	1	2.7	13500	2	2	1.9	11500	3	3	1.1	10000
低碳钢	0.8	4.7	6.5	13	3300		9	12	2	1	2.6	15500	3	2	1.8	13000	2	4	1.1	11500
低碳钢	1.0	5.1	7.1	14	4000		10	13	2	2	2.5	18000	3	3	1.8	14500	2	4	1.0	13000
低碳钢	1.2	5.4	7.7	14	4700		11	14	2	2	2.4	19000	4	3	1.7	16000	3	4	0.9	14000
低碳钢	1.6	6.0	8.8	16	6000		12	16	3	1	2.3	21000	5	4	1.5	18000	4	4	0.8	15500
低碳钢	2.0	6.6	10.0	17	7200		13	17	3	1	2.2	22000	5	5	1.4	19000	6	6	0.7	16500
低碳钢	2.3	7.0	11.0	17	8000		14	19	4	2	2.1	23000	7	6	1.3	20000	6	6	0.7	17000
低碳钢	3.2	8.0	13.6	20	10000		16	20	4	2	1.7	27500	11	7	1.1	22000	6	6	0.6	20000
奥氏体不锈钢	0.23		5.0	10.0	1800	7.0			1	1	2.29	6500	1	2	1.52	4800	2	2	1.09	4200
	0.29		5.5	11.0	2100	7.5			2	1	2.24	6700	2	2	1.48	5400	3	3	1.08	4800
	0.4		6.0	13.0	2700	9.0			2	1	2.16	7600	2	2	1.41	6700	3	3	1.06	6000
	0.6		7.0	13.5	3600	11.0			2	2	2.02	10760	2	2	1.31	8600	3	5	1.03	7800
	0.8		7.0	14.0	4700	13.0			2	2	1.89	13500	2	3	1.22	10700	3	5	1.0	10200
	1.0		7.5	14.0	5700	14.5			3	2	1.79	14500	3	4	1.15	12900	3	6	0.96	12300
	1.2		8.0	14.5	6700	15.0			3	2	1.69	15200	3	4	1.09	14000	4	6	0.93	13200
	1.6		9.5	15.5	8700	16.0			3	2	1.53	16200	3	5	1.03	15400	4	6	0.86	14800
	1.8		10.0	16.0	9700	17.5			4	3	1.47	16500	4	5	1.02	15900	4	8	0.84	15700
	2.0		10.5	16.5	10400	17.5			4	3	1.42	16700	4	6	1.02	16300	4	9	0.8	16200
	2.6		12.0	18.5	12700	20.0			5	3	1.34	17200	5	6	1.0	16800	5	10	0.7	16800
	3.2		13.5	19.5	15000	22.5			5	4	1.27	17800	5	6	0.98	17000	6	13	0.61	17000
	4.0		14.5	21.0	18500	25.5			5	4	1.17	18500	5	6	0.95	17300	6	14	0.46	17300

7 u' F$ v7 Q5 _+ W7 j; X+ A+ S8 q+ L1 q& [1 G2 I2 W/ c3 Z! |. e8 ]7 s) T. W5 H$ l% ^, j6 F3 A- _, }' a" q# A3 \" f# b2 ~# q) u0 y' N! L# d. i8 k* P$ o1 N) G9 g% X2 {; C* U! E6 B' G6 ~% X9 Q" E' n) b9 ?& D* ^8 B$ h9 J2 D, n- A9 v, }9 B+ Z9 w) z( L3 B* f* w2 _ z4 C# z' ]4 ^& X e% O6 n5 K* |8 W# \7 v! f2 k7 H$ d; V/ i

0 u0 Q- g5 M. \1 U2 X$ c 注:	低碳钢说明。
	1.本表所指焊接钢板系热轧后酸洗的软钢板,抗拉强度300-200MPa,焊时须清理表面污物。
	2.电极材料为R．W．M．A 2级。
	① 电极形状如右图。②最小重叠如下图。③通电时间数字当电源为50Hz时应乘以5/6。
注:	奥氏体不锈钢说明。
	1.适用材料为1Cr17Ni7、1Cr18Mn9、0Cr19Ni9、1Cr18Ni9、0Cr17Ni12Mo2、0Cr19Ni13Mo3、0Cr18Ni11Ti、0Cr18Ni11Nb不锈钢板。
	2.电极用相当于R．W．M．A 3级的铜合金。
	3.焊接抗拉强度在1050MPa以上冷轧材料时应使用最大的压力。
	4.电极形状与搭接宽度与1．1．5(1)表注同。
	5.焊接大型工件时,为使工艺性良好,重叠宽度L可增加30%,焊接速度可减小,以便于操作。
	6.为改善焊缝表面成形,用球形电极更好。
	7.断续通电,交流电源60Hz,当电源为50Hz时,通电及休止时间应乘以5/6。