冷挤压钢的球化退火工艺规范

HEATS

" @+ Z# A! z3 l/ L( t1 ?. k. T: B, l( o; s+ n; ~; m7 W% X, N6 @' k# e. ]$ ^$ H5 Q0 e- L9 O7 S. x/ ^& h$ t8 j5 a4 f( X6 V( }" l( {0 X0 u* U3 n/ J) Q1 ]0 O, h2 h# [# K9 q% p8 k5 c- d/ ?8 c4 j# J' X& m1 n& d) J- Q# F9 X! n3 w0 O3 L1 h; ^" ~# Y1 `7 x% {% j, K' A3 E1 z! L3 s- s$ V( f. P/ ^5 O. i: m$ C' O( i4 Q/ Z% F' A9 f% x2 Z" y5 }+ `+ T. j8 o' q( X. m5 _4 M- J- |4 R- `! n5 I' I+ G/ z+ C$ ?- a2 F- T# x6 @1 e$ x% O+ N2 `" F/ T) W- F9 l3 N( @' _* C4 g' ~/ z! M% |3 S2 k: V% _! j4 n9 @2 M% e; G- {1 M6 B0 H. x/ ^* Z, T+ s- h0 C+ ]/ y$ u, `/ S {: V9 g) y* l5 x8 [9 Z3 J* ^& K }2 a: ]5 d. l# f- ]& v8 S! S3 H7 ]3 v& x N/ [" ]+ Z% l+ X9 F' Z; d% T0 ]( ~5 j8 K. D! q; O& A1 \6 x2 d" B% C4 W o- ^9 P* |2 t6 E4 I: Y! ?- i) W+ g1 G" s6 l, Q; n# O( w3 ]$ v, P. R _/ v1 r- j" R* X! N# S R7 K3 M& I Y o$ ]* f2 O* G2 n( X8 b( h" [- P: d* v) H% v* ?7 h8 Q. {4 u8 V% I. I" O, Z9 s$ M7 U; |8 q7 T+ I- f: f9 _( u! W: a `9 i9 `5 X' p, n h; t8 }9 J3 e9 |' G$ N2 O/ i6 d; }1 ~- \* ]( P* v5 D. @* h% k

钢 号	退火前硬度（HB）	加热温 度（℃）	保温时间（h）	等温温度及时间（℃-h）	冷却速度（℃/h）	出炉温度（℃）	退火后硬度（HB）
15Cr,20Cr	170	860±10	3～4	-	<50	<130	300
15Cr,20Cr	170	780±10	2～3	700±10-6～8		125～131	500
15Cr,20Cr	170	720	5～6	-	<50	≤125	450
35,45,40MnB	>180	720	6～7	-	<50	≤145	550
08,15,20	150～180	720	2～3	-	空冷	≤120	-
20MnV,40Cr,50	187～217	950～1000	1～1.5	700-2～2.5	60	140	500
40Cr	-	770±10	4～5	670±10-5～6	炉冷	≤160	500