纯铁、碳素钢的抗蚀渗氮工艺

HEATS

" D1 Q! @4 b5 m8 b6 b1 S9 i* t2 d5 y

4 H! ^7 E" ?* Y. B" Y P, t, Y+ D' G# y+ z, O/ x' i. }" e; U# i" L9 \3 l9 h* v5 C7 u7 A' m& S: m1 l0 d8 @2 h- e* G8 k/ h; j m( m8 K8 E7 e" U9 a! k0 h6 j4 e" W) k6 @" A0 r% Z' s: V3 I. a% H( U3 B: g$ ^/ B% s! H2 `+ O* e; C. U" H* a3 u: d9 V0 I2 f: e o% y, H) v! k! P7 D b2 b5 h$ B+ x5 p6 _# b( `, A2 Z4 @( v, ~3 ?! D V; R, @8 b5 b9 z2 S; n. z9 x8 h. D, @8 x9 B6 L( U- v5 p$ Q/ M0 [1 T; m' R$ k& i# K+ b& G \- Z' y9 i3 g+ H+ O0 g% L6 O# M) _9 f: q) n; P6 O7 D) d% Y. p l9 T0 W$ ?% \ I8 I1 i/ ?; ~5 T3 h2 z4 E( k8 J1 t" J, Y+ H6 E' m* H4 s/ A# i Q+ P8 B6 @6 K, n: {9 d0 a- Q Y" i8 Z3 Y0 v, n) b% d- z9 F6 Y& J! }* P: J8 m* T- m8 S- Y/ o( {! b! C# e( y; z9 I0 G+ [* G, P. E5 l. Z% D. z6 i# j% s: n' b5 V0 P& U3 j" _( Y. u$ S# t, l6 E# d$ H: T. d+ P+ b8 E/ _2 x& k, e' U: A! ?4 D* s0 @7 ]) d/ {- u6 g2 ]/ p! \4 ~( J: p+ P: l8 V" {6 s) u+ C0 M0 f, T6 B' Z5 g, l8 K' n9 u f7 T- }) o7 x$ P* _: K# c! @: t! F i; u6 t% ?8 b+ I9 H/ n+ ]- r" d

牌号	渗氮工艺				ε相层厚度 (μm)
	温度(℃)	时间(h)	氨分解率%	冷却方式
DT(电工纯铁)	6	550±10	30～50	随炉冷至200℃以下空冷,以提高导磁率	20～40
DT	3～4	600±10	30～60	随炉冷至200℃以下空冷,以提高导磁率	20～40
10	6	600±10	45～70	根据要求的性能,零件的精度分别冷至200℃出炉,直接出炉空冷,油冷或水冷	40～80
10	4	600±10	40～70	根据要求的性能,零件的精度分别冷至200℃出炉,直接出炉空冷,油冷或水冷	15～40
20	3	610±10	50～60	根据要求的性能,零件的精度分别冷至200℃出炉,直接出炉空冷,油冷或水冷	17～20
30	3	620～650	40～70	根据要求的性能,零件的精度分别冷至200℃出炉空冷,油冷或水冷	20～60
40,45,40Cr,50以及所有牌号的低碳钢	2～3	600±10	35～55	要求基体具有强韧性的中碳或中碳合金钢零件尽可能水冷或油冷	15～50
40,45,40Cr,50以及所有牌号的低碳钢	0.75～1.5	650±10	45～65	要求基体具有强韧性的中碳或中碳合金钢零件尽可能水冷或油冷	15～50
40,45,40Cr,50以及所有牌号的低碳钢	0.25～0.5	700±10	55～75	要求基体具有强韧性的中碳或中碳合金钢零件尽可能水冷或油冷	15～50