保护气体成分对18-8Ti钢焊缝化学成分和抗晶间腐蚀性能的影响

HEATS

& @8 n3 C7 g4 u+ C W1 c5 G8 j8 |3 l/ ]% J7 ]5 j9 z7 E; p" L: B9 |4 ~* {' k i3 v( Z2 a5 K* E @; n o; [ J5 v3 e! p* I, T+ M' \; r; ~/ f5 m2 W- f9 m+ H0 w o4 G% J o4 e; t* M2 \$ r4 Q! n% f5 V5 E" }! g3 x# u6 v q) X! p4 {4 F. k9 R6 D5 I/ h5 q' P: I# e6 D/ F) {, w8 a& v7 m4 ]& X6 ?' H0 N* u' R, u* ?. ~, g+ y4 o$ }' \+ [; D5 V2 r& V$ G9 D, l8 ~) y% o& R. G: D/ n5 N% g0 U: |# D3 Q8 x% T9 I! k0 J4 ^% U, d4 |5 l0 L; x \. K3 d7 c( M8 R, m& d" k) f5 \& }$ p! i7 M. z: W+ Q9 G: Z' P) ]5 A/ h' e! d8 H# K: O; j4 s( J+ @5 r! v6 n0 {' S. v0 q: j/ ^% k: P- ?$ J7 s2 }" G" ~" y4 {& q/ j& k( O+ |: B- X2 J! _6 w* D* J* \. o2 w2 c; n. {6 b4 @3 e! @( Q' `7 J# E! h! ~: I4 K% |, F5 h% O8 X; {: k$ i' u% e- d) `: z8 z( r2 c/ _+ c3 q' C* n- w( d3 k4 n2 ^" N- S/ u, P1 G8 R* A! j. n5 d8 Q* B) P+ I# `* \/ u7 ^7 }. m: F% J9 ]5 l) x4 j) y- p" M% v8 C* L `) h2 C/ R L2 v, A3 W) W+ j) X' X% h7 a7 r: n5 h2 X, z+ ?8 |/ ^; s& e/ @5 U2 \- a# \1 p$ `1 L( c; j/ z. m, N2 f! w2 L4 C9 R* V9 L6 C7 q9 Z- V+ K/ _% U( f! C" e& m. L0 l% A2 Y7 G; _! C0 ]$ l, D

金 属 种 类	化    学    成    分    (%)								65％硝酸沸腾72h
	C	Mn	Si	Ni	Cr	Nb	Ti	Nb/C
焊丝	0.055	0.70	0.62	8.27	18.63	0.83	0.02	-	-
母材	0.11	0.75	0.77	8.12	18.57	0.01	0.57	-	-
在CO2中	0.13	0.51	0.46	8.37	18.32	0.63	0.02	4.8	严重腐蚀
在Ar80%+CO220%中	0.095	0.62	0.56	8.30	18.54	0.79	0.04	13.0	严重腐蚀
在Ar99%+O21%中	0.06	0.68	0.60	8.30	18.62	0.79	0.04	8.25	轻微腐蚀
在Ar80%+CO215%+O25%中	0.08	0.60	0.57	8.30	18.88	0.83	-	10.4	轻微腐蚀