低碳钢、奥氏体不锈钢缝焊的焊接工艺参数

HEATS

* g, A4 D9 P0 w5 J9 K' v4 F' |: U* n" y( W" ~4 i, W' A4 Z. A# ^; ` x j, ^, P9 i* x& f2 \) m5 J5 p( \. ^2 v$ b6 D+ H/ O5 \) _5 K" {: H4 |+ t* {* h; _+ p' q. j2 [2 r3 q1 v6 M( s6 T; M8 C$ Z# ?/ f# o$ W2 ]& H7 M' o' @7 ~8 \ {" I: s$ }( y9 q9 w+ `) Z6 _# }3 e* W# i# e1 t9 h* {2 ?- w! B) {# \- r1 z5 G+ N. F J+ n, P5 C8 m7 S( O: u* D. t% P3 B$ P3 G6 s, F8 b! s& m I2 m' j5 z: p5 T. g7 A% @7 B+ a8 U* @, p& I9 T% y) a$ L( R" I% c. I: c$ {$ k0 g, H; X2 O6 Z( t5 ~ U [; H/ W! X' Y U6 i1 |4 ~$ y( l- C7 j, r. N4 c f2 G9 t2 I0 ~% k+ m/ g: f" I; ^& ?2 }( r8 {" [; O6 V/ h, ^1 a' \- I3 I) ]& ^" l& |: G0 x8 a% t' u/ O' R& ]& G: v# v5 `) b; u: m2 W& y) Z1 ^! w+ e# _. M; G9 n; m) I @' f9 E6 }4 K& m5 d6 G* N2 I% d- r/ f/ M! I3 _" z+ B! h% A" h% h r0 r; ~! E! R4 a/ ]; r, T) D& I$ ~& Z5 ^2 m8 O2 L. o( Z" l/ |5 |) P5 N W1 ^) `, n0 H; }1 m' i) g' [. @& U" ?: V1 Q8 X" U9 z5 ~8 E' l2 ?% p! b0 }7 N/ d1 {0 i, n1 Z3 i. y9 _' w* Y# q! V! Q* K0 f6 X7 S$ p( f o# _, y3 d% j$ M2 h k! T7 B1 D v# \$ C% ^9 D9 H. u% w* \# ~- X: h9 t, l: V' L$ u4 E3 |5 o: M8 q7 s7 [* x/ m! B% o1 y( }7 c8 D! I) u! O- m" f" f% J! D9 c6 t, S f$ `" Z8 s; k( V" R, [2 _6 P4 X8 a# w" F- ?7 r& t6 Z/ q! c( d+ y+ ]3 B/ e! G" Z: f- O* J- g2 u& g( V+ l. v5 c0 E* R7 Z3 n& @5 r# c. k. \/ F; q* I @! ~6 Q/ J+ T. O- W0 g' t7 Z6 y( R- x' A8 z- @5 e' B X9 G! m6 z+ ~/ e& {5 {$ E" i+ Z8 Z4 F6 F. o0 a' b9 p% r. L# R1 b9 W3 Q! ~1 N! w8 y$ U# u6 @1 j: ^; A1 v) o' a$ I# Q0 b! M4 {5 f7 T( j$ I" W5 T& k: M* n$ s8 @, J! R& w+ @* P! J9 e( P" X1 `' Y/ W! z* Q& A( J8 B7 i7 A$ b) W, b- p+ r. m6 ^- d `2 ~# |# @( U3 f0 e' ^* l7 ]4 S4 f/ W6 X* [2 j7 p- g! V9 v! z3 X7 O8 m4 Z( Z' J5 C' U* C2 `; d/ G9 S, \# K0 p- ?. [2 c) ^3 ]7 u* }/ y. R; V- w' s" W9 b: g: B) c9 E _' b2 J7 `: b% z( K, A9 G# n8 \! y: j1 k- N: J) t% M9 s9 Z4 G* k8 {; t9 p# {6 q8 u; v9 t& U! Z% Z3 H* C9 P9 f6 z: R, S8 x* i: Z. E. e# s) p6 V- b) l# c1 O7 U0 g, A) e2 Q4 p; ~) A# e! R. n" f4 Z1 n! ^0 Y2 N& [% H' c& ~1 D1 y! H h1 R' g/ \8 G- E2 ? H4 e/ t4 h0 ^" ?, E3 u4 x& F6 y) J1 @9 S c: F. n# q8 W5 }& V0 P# H6 Y! l+ @8 g# i! Z( t3 w3 |; p+ f. M& v' ^. q# o( Y2 c' o2 W; a0 Z' B7 [" A* k. ]) l K, m1 `' l% I7 x' g3 ^4 J/ ^" E) {/ k h2 Q) D: ~. g. @% K* ~) G' P6 j' F7 @ w. b) n% P2 g5 ~; Q' O$ o* h1 I5 {7 E- `8 i5 J3 z) m8 E$ p/ P- F6 O1 P/ y" }1 r! E( J# a# s4 _2 ~+ r1 I8 R" z/ G5 H; E& X' S( h; W' i. B. K4 V7 U# ~, n6 A. \; y$ Z- q3 t% `$ S7 j' K( R" g( p4 E# F2 B1 X" B7 O) G8 c" J1 E; q# ~$ Y. }9 E4 T; \$ @+ A; A1 X* g( @1 w* o( G* k: w$ u# Z3 m# i% A# U4 _' o2 I0 X x0 n# f- }' I3 I: p5 B. o9 _! ^$ ?! z, O. g' R: v x/ C3 G5 I0 T, \0 @6 z' P' d3 Y0 j9 Z* {/ H8 h6 Y: P( H+ h1 c& k, T8 \7 U8 }8 P8 }7 A7 L5 O& V; B6 P8 f; _* j) i8 H, ?. {/ ^- G, D$ L( a( N0 G; F+ ^- |2 U; Q' ~/ v n4 t9 @ r9 s9 t; o4 x$ X( y: \4 P- I( u2 L' t% F/ }, F, i1 t1 A9 `5 f2 \$ A- X2 _8 r1 C# t; S* ?: l( S# g! S$ \2 v4 X# }/ k, M# N- S( o) G$ I3 m' E6 N" g$ W* Q1 W; O, T" v. r4 W) o% V) b3 W3 N8 P, t G/ q. I6 U* }# K: A9 \) o# W, Q+ F3 S: ~& R6 Y, I7 ^% {( o& u1 o2 ]- _, u. l; k! l. t& H: Z& Y1 A+ M# g4 W# u- y! d5 {/ ? j2 D& B' I$ g4 n3 G* S/ L- m5 b0 d* A" M. x, [2 p; A; j: x: w. @* L5 y; y8 R* t- u4 G1 \; x! d" D! t% j/ n( v0 C: R5 s: g. ^: ]0 Z# z8 c+ \' C% |" o( H% F8 |6 r6 { y* X2 l6 G/ B; e+ ~: O9 V5 F1 |' b' D P* Q! U- {" D, y# n ` y- U2 T- J5 k; W( z* d" Q2 t; s- g6 s7 r; _: q% v7 a4 }8 P8 P5 `" P$ r( m, T" K3 ^# U- z9 c! D- E' y7 ~7 T4 h: u; P+ `) L6 e8 B% ^! s! A" }4 E+ y8 p! C2 f) z+ q8 n4 b* U% C/ {' Q) E- m2 Y- s" s0 G# y, }; X. ~0 J3 |3 E; S8 M3 g/ c! Z. s3 D9 O$ ~& m; t% m* r! d; p! }" N8 Z% y: k! V1 s' G0 Q$ x! P' @. M& n( @7 [. e- z3 u* n: _/ E+ [9 k( @9 R+ W1 P* k8 {; H+ E: A& L! c5 K1 Y7 D6 V" C" o5 S2 Y' }! Q7 r3 U6 e- s, k2 A7 R7 ], i/ u; q- x7 i; q, ? O! d% N; `. x, W, f) }8 Q4 ^4 p4 K0 i2 d% Q$ D J1 }0 P5 w$ T1 t3 @! Q$ w/ m, v* K/ T A* L4 p9 l" g9 @) N- W9 G/ Q2 D* \! o( g8 a5 Q8 @6 W' C+ ]1 y9 H+ E9 U: P7 c8 x- q8 L* ?3 l8 ]& m* b& @8 F. D) u* h* V( o# f5 f7 c: X$ c6 N/ f' c# B$ z) X5 N7 M% U# U; f3 Y: C4 z# E4 I5 @& L1 }9 m; c& U4 k ^" t4 R/ z2 A9 Y4 \& N2 ?4 t8 A" N/ v/ m1 D' u/ G; t$ G6 k6 b3 I0 @; j+ L5 u! Q5 O; o5 H1 u# A! l7 `8 p& R2 `5 M- v* ^+ O- \, ?/ v7 d/ ^5 h% H4 G: `& g n; ` o% i0 p/ y3 ^8 w; D( z: H* o5 ^2 `, o4 h+ `$ P5 M$ D+ S: B1 _( `0 K5 j4 r7 f. G/ }1 I, c: b8 ~4 k) B+ k" L3 B: v) f6 q( Q {: e' _3 G; X& b$ ?& ?" r* |! u- y. J v- B; q) G* J3 s: e9 V. U, _4 a: L( L8 @; H Y+ C% ]7 r0 i0 @0 U! G1 J; ]: a" l# w8 L& P# F+ T# N* ?0 V2 ]4 A* E- y W. D1 D4 g# y) ~3 ^+ C% q7 |, G9 g* f" p% p6 {# a+ y, \. a, V5 I I, ]/ M- n- H: c: K) ?: [ i; A. m3 s9 M; ]* `$ M4 t7 Z& {' ^ D% M6 Q* T5 v, e8 S7 E! d% a/ e9 U A0 g7 C- e4 ~: j' }6 U. k$ I3 U+ D9 ^; [1 `( ?/ M; ^0 z1 K1 c8 K5 } k; L3 U% E; M8 @5 j3 T" K5 G4 Y+ _, U7 I6 K$ G4 F4 W. K4 w! x* U; Y0 f' n$ E$ m1 X% k, _) q" z* J' ^- C0 n$ b& e0 P$ X, ^4 b" F) O9 b1 [8 a6 s5 \1 R: W; X- D" b2 ~4 S8 j+ G, Y3 c; `: ~- z7 r- A6 E% \8 T( E% d L. o% f, m Y; T r: c( _( ^0 A: K4 Z( D9 w% W6 Q1 F0 p2 O, |1 f. M, ^) f# w; Q+ V6 }2 g* a, Q9 z' S* o0 w5 A! w* o9 `7 w5 r: a4 f* q+ j" k1 g: Z# V/ ]# B$ N; ^0 w* l/ d4 @0 B& ]( S% k2 p t& Y0 l4 d' h" Y% R0 ]1 h7 O' F6 E0 d4 Q9 w7 _0 r! _. @/ V9 N# i# B8 Y: R3 a/ q' w' W; k1 T6 l! u- Q9 D. b& i. e8 y5 i* K0 p" N0 g' Y' d6 C) E' b3 R! T) D6 V$ D, c, m/ j; S2 h" I& H. K* V6 \" s0 q. |2 q( v# z' q8 t* g- M, A& v/ x3 y ~1 r6 i. g) ]& z$ I2 S7 m# {+ y. N3 l. y7 B5 Z" ~2 Y1 `9 m- Y) u- {# W( @: m& K: `# z: m0 ?& u4 y/ |6 Y6 r9 m# x9 i. t9 D" ^/ P& V; d0 E+ e) ^* s5 ^; [: f2 ~7 x* Y9 w7 [1 d7 ~- q X6 H5 }- R: c% o' x* ~# a7 U3 N+ Z* O1 T: |9 J- t/ d9 g; \( j5 ~4 I {# E; [- a8 r9 o- E: H% ]$ |& f5 ?8 m, I- \" D8 J' A# X0 ^9 f2 b: O4 C5 j, S, \% D* ?$ Q! K+ @4 K7 {- v3 ?+ ~! S& G5 e; H2 I) M1 w" D! m! {; ~. I5 j# N. } p# g2 K) V9 Q6 a8 y* V6 e/ k2 Q" G+ X K' b4 D* z# J6 m6 p6 G' \& q6 G5 h+ y" w3 l0 L0 s! b/ e, f, M! q& f$ j7 @& L3 C ]& w' _9 ]* C; q; ?) w+ S+ p0 v# n! ]+ b# o% K" y( O E8 v2 M; T2 w$ Q2 x) a1 a0 i0 D4 O% E* t, k2 T' V. |# M# X+ x5 l# R* Y y+ w, u% S. J7 n0 @* Q2 s( F+ i

材  料	等厚搭接板的板厚 (mm)	滚轮电极厚度D及表面宽度d① (mm)			电极压力 (N)	最小重叠宽度L (mm)	最小重叠宽度L② (mm)		气    密    焊    缝
									高  速  焊  接				中  速  焊  接				低  速  焊  接
		最小d	标准d	最小D			d用最小值时	d用标准值时	焊接通电时间③ (周波数)	休止时间 (周波数)	焊接速度 (m/min)	焊接电流 (A)	焊接通电时间 (周波数)	休止时间 (周波数)	焊接速度 (m/min)	焊接电流 (A)	焊接通电时间 (周波数)	休止时间 (周波数)	焊接速度 (m/min)	焊接电流 (A)
低碳钢	0.4	3.7	5.3	11	2200		7	10	2	1	2.8	12000	2	2	2.0	9500	3	3	1.2	8500
低碳钢	0.6	4.2	5.9	12	2800		8	11	2	1	2.7	13500	2	2	1.9	11500	3	3	1.1	10000
低碳钢	0.8	4.7	6.5	13	3300		9	12	2	1	2.6	15500	3	2	1.8	13000	2	4	1.1	11500
低碳钢	1.0	5.1	7.1	14	4000		10	13	2	2	2.5	18000	3	3	1.8	14500	2	4	1.0	13000
低碳钢	1.2	5.4	7.7	14	4700		11	14	2	2	2.4	19000	4	3	1.7	16000	3	4	0.9	14000
低碳钢	1.6	6.0	8.8	16	6000		12	16	3	1	2.3	21000	5	4	1.5	18000	4	4	0.8	15500
低碳钢	2.0	6.6	10.0	17	7200		13	17	3	1	2.2	22000	5	5	1.4	19000	6	6	0.7	16500
低碳钢	2.3	7.0	11.0	17	8000		14	19	4	2	2.1	23000	7	6	1.3	20000	6	6	0.7	17000
低碳钢	3.2	8.0	13.6	20	10000		16	20	4	2	1.7	27500	11	7	1.1	22000	6	6	0.6	20000
奥氏体不锈钢	0.23		5.0	10.0	1800	7.0			1	1	2.29	6500	1	2	1.52	4800	2	2	1.09	4200
	0.29		5.5	11.0	2100	7.5			2	1	2.24	6700	2	2	1.48	5400	3	3	1.08	4800
	0.4		6.0	13.0	2700	9.0			2	1	2.16	7600	2	2	1.41	6700	3	3	1.06	6000
	0.6		7.0	13.5	3600	11.0			2	2	2.02	10760	2	2	1.31	8600	3	5	1.03	7800
	0.8		7.0	14.0	4700	13.0			2	2	1.89	13500	2	3	1.22	10700	3	5	1.0	10200
	1.0		7.5	14.0	5700	14.5			3	2	1.79	14500	3	4	1.15	12900	3	6	0.96	12300
	1.2		8.0	14.5	6700	15.0			3	2	1.69	15200	3	4	1.09	14000	4	6	0.93	13200
	1.6		9.5	15.5	8700	16.0			3	2	1.53	16200	3	5	1.03	15400	4	6	0.86	14800
	1.8		10.0	16.0	9700	17.5			4	3	1.47	16500	4	5	1.02	15900	4	8	0.84	15700
	2.0		10.5	16.5	10400	17.5			4	3	1.42	16700	4	6	1.02	16300	4	9	0.8	16200
	2.6		12.0	18.5	12700	20.0			5	3	1.34	17200	5	6	1.0	16800	5	10	0.7	16800
	3.2		13.5	19.5	15000	22.5			5	4	1.27	17800	5	6	0.98	17000	6	13	0.61	17000
	4.0		14.5	21.0	18500	25.5			5	4	1.17	18500	5	6	0.95	17300	6	14	0.46	17300

6 v$ U8 q* ?7 ?- z* n' E! j& p; L3 C& v2 }, o: U; }% y' W6 _2 l2 y# v: y; s6 }# {7 V; d9 E% i: P. R: W! r/ C t: w, I' u3 H; [. N7 x- H/ a6 N5 u5 r" X" i% {! N/ a, B5 M! t" N, ?- a) b: L8 ^3 u, }/ z. T x2 Z8 U" G7 E3 Z9 E6 { E4 s6 l5 C0 ~7 J) z# W; n& D8 h. D: _& e! q9 Z# m% Q) T4 N2 `8 r9 j' ]& p4 s: |5 t* Q3 F$ r# R) Y, h/ |3 R. W( Z/ W* p/ a1 K: g3 m1 G6 t* h3 `/ C# Q4 F5 ]" Y: O" Z) c6 ]$ ?4 F2 C4 V: [; F" q a1 d+ s9 O7 X0 N( i, q F8 k |( X, w0 s+ \, }; h6 a

注:	低碳钢说明。
	1.本表所指焊接钢板系热轧后酸洗的软钢板,抗拉强度300-200MPa,焊时须清理表面污物。
	2.电极材料为R．W．M．A 2级。
	① 电极形状如右图。②最小重叠如下图。③通电时间数字当电源为50Hz时应乘以5/6。
注:	奥氏体不锈钢说明。
	1.适用材料为1Cr17Ni7、1Cr18Mn9、0Cr19Ni9、1Cr18Ni9、0Cr17Ni12Mo2、0Cr19Ni13Mo3、0Cr18Ni11Ti、0Cr18Ni11Nb不锈钢板。
	2.电极用相当于R．W．M．A 3级的铜合金。
	3.焊接抗拉强度在1050MPa以上冷轧材料时应使用最大的压力。
	4.电极形状与搭接宽度与1．1．5(1)表注同。
	5.焊接大型工件时,为使工艺性良好,重叠宽度L可增加30%,焊接速度可减小,以便于操作。
	6.为改善焊缝表面成形,用球形电极更好。
	7.断续通电,交流电源60Hz,当电源为50Hz时,通电及休止时间应乘以5/6。