低合金钢用实芯焊丝和焊棒对照表

HEATS

0 @$ {6 @% k Q( G. j4 q. q2 W0 m' d# ~) z4 r. p& I0 E, ^: F' K: J8 |2 S4 }+ k6 e7 s, r7 j4 d! S& O- o2 H1 s9 p1 \/ q; l' ^: n/ f3 m( n6 p4 p/ r! _+ T3 [8 O7 V2 G, R( Y) t" _8 m3 [5 C* w% j- H! q8 R, Q' r& b4 d) ~. u# @- s4 ?- w+ {+ Y; R% |; E& w% D$ `& G( N/ Q$ ]9 z* F" G% Y; v. r, T) m- E% s# e# K; E$ g+ P6 G9 D0 R) L }* [! l# G1 `1 x, @) Z) z1 G/ i/ x! ^1 b$ b6 z2 n+ ]$ B% Y7 v4 K8 z# ^: {, g- s C$ L3 ]/ M' N5 s! }: H2 k: z' H9 x, T+ t+ z6 I/ e2 z: o0 o9 f6 ?& M) E) ?, p" {6 e! K( G7 k; u9 n* |0 H/ Z" H) [# O. E |+ V6 I+ \4 l' _. I: [. ~' L0 P. O" E8 I. Y+ a1 z0 Y+ X& @: h% Y0 t+ G+ R0 ^6 e. H* k" |6 R/ M8 z* V) x9 m9 `5 r; ?/ @# j; e/ h+ ~+ P8 _4 ^$ F/ n8 W: L. Q& h9 C4 R6 C3 ]5 B* f/ P, O5 ~3 A# L- B% N" |" ~( U$ ^" B$ w% R) j% n$ J( o/ ]3 C3 s& C1 q0 O! Z9 m2 l* a4 h) {: @ `4 ^( Q- l& g4 p0 T( Q2 x; H ~8 v- K! ~0 r5 h& U, G1 K) {9 |9 g7 R6 U2 J- X) H4 L$ m2 V) k @$ h( Q6 Y2 w. Z3 y' `" b# z7 L' I# V# v& K7 S5 R3 ?1 _+ a6 E3 l* ~& g/ r& P- {/ Q! c* p4 s, b* H$ _, k( E. r% ?% E8 L% P7 r. i* W N* t" `0 G6 d6 V9 K+ G- V0 d. s0 c9 i, M) q3 H% S9 _# C6 M) K( F$ O& x# z) N1 N$ Y( O; i5 c: K3 b: P6 j2 c% v: D5 M1 G8 Z3 L4 B( F6 o- Z7 J% \: w& p) s6 C! q5 Y

中 国	美 国	德 国		瑞 典	瑞 士	荷 兰	日 本
GB	AWS	DIN	THYSSEN	ESAB	UTP	FILARC	JIS	神钢	新日铁
ER55-B2	ER80S-B2	SG CrMo1		OK Autrod 13.12 OK Tigrod 13.12	UTP A 641	PZ 6042 PZ 6542
ER62-B3	ER90S-B3	SG CrMo2		OK Autrod 13.22 OK Tigrod 13.22	UTP A 640	PZ 6043 PZ 6543
ER55-C1	ER80S-Ni1			OK Autrod 13.26
ER55-C2	ER80S-Ni2		Uniox Ni2.5		UTP A 6025	PZ 6040 PZ 6540
ER55-D2	ER80S-D2	SG Mo		OK Autrod 13.09 OK Tigrod 13.09	UTP A642	PZ 6041 PZ 6541	YGW 23		YM-18
	ER80S-G	SG Mo SG CrMo1	Uniox I Mo Uniox I CrMo				YGW 17 YGW 21 YGW 23	MG-60 MGW-50B MGW-50TB MGW-588	YM-53E YM-60C YM-60A YM-60S
	ER100S-G					PZ 6047 PZ 6547 PZ 6048 PZ 6548			YM-70C YM-70A YT-70