马氏体型不锈钢的化学成分

HEATS

 

! `7 l/ [6 N# z( b! d6 R2 E3 U1 _* e3 R8 J; I7 T8 |6 j0 f/ R2 x5 n, p3 S( b2 D/ N- K8 K. i2 x! d- j' B o8 U$ W S2 O/ @! W; B W6 [ z9 r" L6 |/ ~9 H- A( g {7 h5 b" _: M9 `# R2 r4 B! @# T0 L6 q4 u4 F/ ]3 U H3 M. H# e# J; x k7 d T3 Z C# I! {9 A( F$ H6 v$ s! C6 ^0 O0 Z& d; J+ T7 O$ q1 w; I; O! d B8 a# ~/ c6 c4 n& q2 M+ c$ E }# i) o( ]5 \! H! n1 R+ l' ]! C; U3 R# ~, s, w+ [' F* P, @7 w1 d; I+ T8 K B9 @! [/ W+ a1 X) X/ d9 r8 V' @% ~& T* x6 B' W& ]( W) V9 A, F* `* t- ?1 K) p- d8 J2 [" M9 k" ]2 E1 d' o" S& y# X: J1 x3 W. `" b( \8 @) l: N1 X$ f! t; b' v& w2 ^4 X# s6 |/ x$ D% @6 B; h2 q2 O, `3 n# O. n" w5 |( a8 ?( N: a" p* `2 H7 i# X7 L) t0 g0 p2 Z( W8 Y1 b" k, K0 \9 v3 R# f9 h" j' J* A9 e8 x1 C' `$ r/ K4 }. ?, }8 |4 b: s5 C1 Q. k4 m) i+ r* Z# j. N" c0 I' r1 G- B2 S1 s- l- e6 i( Y7 H r. I5 F% G0 }$ t) m/ ?' f9 Y$ H+ S' ^) \% L+ {/ Y; H9 P: \& Y( Q$ S) [. `7 X' {9 |6 n$ ~% ]% B8 @: K; X. @& [( c& A7 V/ l( C/ w% L$ q b& F% q$ z8 M% g# n( U3 Y N/ Y3 L( B/ y2 g5 _ b. B- ^" V J# Q0 L; m7 q9 ^' F# [% t, F6 F P- w$ L* U$ ]! g! {0 R' c) z9 {/ L5 {/ p5 L# ?) u5 d1 T3 w( k, @; a' G% d

牌  号	化   学   成   分   (%)
	C	Si	Mn	P	S	Cr	其  它
1Cr12	≤0.15	≤0.50	≤1.00	≤0.035	≤0.030	11.50-13.00	①
1Cr13	≤0.15	≤1.00	≤1.00	≤0.035	≤0.030	11.50-13.50	①
0Cr13	≤0.08	≤1.00	≤1.00	≤0.035	≤0.030	11.50-13.50	①
2Cr13	0.16-0.25	≤1.00	≤1.00	≤0.035	≤0.030	12.00-14.00	①
3Cr13	0.26-0.40	≤1.00	≤1.00	≤0.035	≤0.030	12.00-14.00	①
3Cr16	0.28-0.40	≤1.00	≤1.00	≤0.035	≤0.035	15.00-17.00	①
7Cr17	0.60-0.75	≤1.00	≤1.00	≤0.035	≤0.030	16.00-18.00	①②
1Cr17Ni2	0.11-0.17	≤0.80	≤0.80	≤0.035	≤0.030	16.00-18.00	Ni1.50-2.50

% J7 u$ z3 a: b. f1 _0 G: J% V+ G% \4 K$ E6 M" a6 v4 F' {$ r; A- j# Y, V! |; ~4 I5 t; Q( w9 y' z' E0 ?7 y- f: F( k3 ]' G6 m$ q8 h9 u! B! F, h* i4 T* D% h$ A# l" f6 ?6 P% n

注:	①允许含有小于等于Ni0.60%。
	②7Cr17允许含有小于等于Mo0.75%。