高温用合金铸钢与不锈铸钢的力学性能

HEATS

5 V/ l7 f0 {+ B4 }& D n R" T+ O4 b( v" e( u7 J/ K; O# H1 ^8 g; c- @: m9 d+ B. i' a/ d! x l o4 N1 c1 T, b6 n1 h a5 X2 L7 G# ^4 S- ^( c+ }9 ?+ ]/ l u5 u- w/ U, A. Y& Z6 n2 u4 n+ p- }( _( q4 h+ _+ E0 M/ v& r" e! y8 m( v+ V) x1 Z; c4 x, m- d4 S" K; K' `$ Q$ t8 ^4 F0 A8 U. Z- J) i4 W. U' j h: T. `- H) U! k/ R6 d. I$ B& x; H, d4 R( v0 N' P T& z" Z J+ [* J* e6 k% f) l1 a, X& T# n; a P3 M* z+ H% {) A- p% j% ~7 l" C; y M- m% i7 X3 R' R& R: e: r' h1 t; m( y& T; K, q% |! A9 q+ E8 [) t& |! [# R4 X5 M! V' V O; {# Y% a$ x! Y/ {/ ~4 F3 J$ E& M( Q+ z& N" N$ r( O7 V) g$ V1 b$ a- ?4 Q! @- S: _" I( }+ {9 u& v0 q: H+ q ~0 W$ N8 D3 _$ B* D3 ~4 [2 M: r- Z# h% W1 w3 p0 G; x3 ^+ L4 a+ G) v" c7 T! @" E1 ~% @. @! b4 X5 N% r; H* y5 W. V3 R# C& n$ @3 [) { P. u- R+ T$ S4 t+ n$ \. h) \& K5 t& l) L( @; V2 t% g( F1 S5 _' n2 S& O# U7 R9 O! p9 l6 @1 ~% o1 M6 d+ \# C8 x3 d# d* k$ s, U2 _, k. X3 Q; y! Z# j1 w( e& q6 R3 [, q K& ~( j& t# |5 p- x6 n+ ~! C1 }* D$ j1 y- P! b: K: q& ~8 C( j* S/ a- U" K+ }$ K H' I; D, D, A. e: L: x$ Y

. b) f$ \% p3 Y( P- i6 n 钢 号		5 d$ v. b0 L) ~ 力学性能（不小于）				最低预热 温度/℃
ASTM	UNS	* o6 V, z8 {: {+ d σb/MPa	σs/MPa	- y1 O0 A5 ?, k. S# `1 N δ (%)	F \# j3 B: l6 b/ @. H φ(%)
WC1	J12524	450～620	240	24	35	10(厚度≤15.9mm时) 120(厚度>15.9mm时)
WC4	J12082	485～655	275	20	35	150
WC5	J22000	485～655	275	20	35	150
WC6	J12072	485～655	275	20	35	150
WC9	J21890	485～655	275	20	35	200
WC11	J11872	550～725	345	18	45	150
C5	J42045	620～795	415	18	35	200
C12	J82090	620～795	415	18	35	200
C12A	J84090	585～760	415	20	45	200
CA15	J91150	620～795	450	18	30	200