$ [( P2 B# g' W. w. A* L9 h+ ~0 y! N; J: b5 E2 j9 ?# b0 I' V- g- B8 P- J" Z% D% |' y- a' M9 s6 f3 P: Z, x8 B9 x7 ?0 p/ ?( E+ j5 C. w4 h( V- r" F; z8 j9 P+ {! X' F0 X( }) x, B6 [) P+ [0 `: K1 ]/ Z6 W& J$ ^7 x- }5 F- Y* ^2 l. m$ h; h6 f, L; S8 _# x- \/ `% T: }: Q+ E8 t! `) ~2 S0 K4 G2 I# |% H7 V1 `0 C- g+ A. K0 r+ z5 y6 \6 {6 l" f I& K" j) z# b* B9 H6 w4 E% L2 i( y- g# N, Q, F* b3 |% o5 {& L! `+ T# N3 t7 I: L3 V5 J" @. R/ t8 F" K* @ M* g5 O9 a; S$ A1 x' T! r9 g+ i2 \8 ?/ E# I5 x9 S! V5 w9 F( b) a# u9 u! i C5 V$ d' P& A, y6 ]* L7 b0 t$ i' x5 V3 u, U( v( o X! M" f* A( b Q& g v2 b, W. u9 b/ M0 }- a7 [3 L8 K/ P- n/ f+ Q. m; N: L* _) Y7 x, g' V4 U8 t7 l# R" Y+ I9 R/ {8 [# r% D1 x+ ^7 r$ {) T- Z# x. K0 d( j1 Y, ^2 q( J" H( _. {8 v6 V6 r: A& S) u! U' P3 E4 q# L, ]1 L3 E1 c% w: x' l9 H0 q/ R* e, j; ^- ~% ^5 V$ E0 j) s; ?* M6 u. B% g( Z1 U8 S3 _9 I; ^+ ~6 A7 F. {8 N4 n- q: Y0 C# g& z& c+ g& |9 J3 P7 P1 o F/ K ?* t# Z- m# v6 p% \+ F( u A; w$ ^1 ^7 m" `( T; r( O; R. E2 ]1 Z! ?' _* Z6 |4 ^& ~3 D5 G% Q+ g& q, L# h6 o% N7 W2 @+ _

铸铁种类	铸件种类	阻碍收缩率下限(%)	阻碍收缩率上限(%)	自由收缩收缩率下限(%)	自由收缩收缩率上限(%)
灰铸铁	中小型铸件	.8	1	.9	1.1
灰铸铁	大中型铸件	.7	.9	.8	1
灰铸铁	特大型铸件	.6	.8	.7	.9
灰铸铁	圆筒长度方向	.7	.9	.8	1
灰铸铁	圆筒直径方向	.5	.5	.6	.8
球墨铸铁	珠光体组织	.8	1.2	1	1.3
球墨铸铁	铁素体组织	.6	1.2	.8	1.2
可锻铸铁	珠光体组织	1.2	1.8	1.5	2
可锻铸铁	铁素体组织	1	1.3	1.2	1.5
白口铸铁	一般	1.5	1.5	1.75	1.75

9 F9 a! _* y$ n& b