浇注时铸件全在上型的静压头

HEATS

! w3 f( k7 J* P5 B" y' ? @# T2 }( S5 S0 {8 ~0 j3 Q3 L% [3 K5 g. o& b+ ]( k" ]1 I: o' \; x2 w3 u7 K7 @9 R9 d( c, J" V# I0 h1 e+ g B( _, ~6 C/ E A9 Z5 o' x6 u$ H' p+ B2 e% C2 X1 j4 @+ k5 n. R) {% g- n- N% J7 r% s6 M8 p P0 K# O) m$ B$ m0 A/ l6 n |, t1 g- i) S& b1 A Y S9 w6 S6 Q6 B0 Z" \, j( K% l# P) f% h0 P$ B& }7 ]) W: I [$ b7 |, [; o/ u5 T! |2 y7 G4 S" x$ @( X% j& C$ x% L+ l: Z5 y! S2 V1 F3 R" j/ }& l% ]" N( g. C+ s8 n8 I. |8 E+ u& ~! q+ ] N+ t1 p& L6 `% m, e# ^% k- v2 y! o& @; @! J; a4 b) @% \6 y% @# z) R8 `* e$ b$ k2 N0 k- Q! V1 c B' v$ q' F& M3 T5 u D% v3 {- v3 P4 R8 E; Q1 j5 _! i( |% x4 f1 v; _' s5 N1 ?( c ~2 ]) y0 A8 Y; L/ Y7 r) q1 ~6 q2 k) P& V2 }8 q8 j0 C: ~& e, a8 N, J, z- z2 U1 f. T. k( v P. W" Q+ |2 @5 k8 F5 j' N5 V& |, o9 D6 e5 k9 ?/ I; G& C7 k/ `& `! w! _" e/ c, ^* r4 m$ Q( I3 I+ |4 F1 h9 c1 u5 j5 f s% L4 r7 h& d" f6 [5 P/ }( ?( g2 n) W, u+ R* {$ d/ R2 d) Q( v/ D4 r; t- U3 B' A/ I+ U3 F+ s6 p! S: G2 R% c* d- F3 T( `: }0 g5 F( W( j) R( }- v/ E! i" I# E0 j- t0 s4 J! }* [0 W% M0 u+ U3 q9 l; o! @8 }! }

铸件高度	上砂箱高	浇口杯高	顶注静压头(mm)	底注静压头(mm)	备注
50	100	150	20	23	分型面在铸件1/2以下,距底面很近时,视铸件全在上箱.
50	150	150	25	28	分型面在铸件1/2以下,距底面很近时,视铸件全在上箱.
50	200	150	30	33	分型面在铸件1/2以下,距底面很近时,视铸件全在上箱.
100	150	150	20	25	分型面在铸件1/2以下,距底面很近时,视铸件全在上箱.
100	200	150	25	30	分型面在铸件1/2以下,距底面很近时,视铸件全在上箱.
100	250	150	30	35	分型面在铸件1/2以下,距底面很近时,视铸件全在上箱.
150	200	150	20	28	分型面在铸件1/2以下,距底面很近时,视铸件全在上箱.
150	250	150	25	33	分型面在铸件1/2以下,距底面很近时,视铸件全在上箱.
150	300	150	30	38	分型面在铸件1/2以下,距底面很近时,视铸件全在上箱.
200	300	150	25	35	分型面在铸件1/2以下,距底面很近时,视铸件全在上箱.